{"id":5567,"date":"2025-12-19T08:44:19","date_gmt":"2025-12-19T08:44:19","guid":{"rendered":"https:\/\/korea-transmission.com\/?p=5567"},"modified":"2025-12-19T08:44:19","modified_gmt":"2025-12-19T08:44:19","slug":"technical-standards-for-fasteners-in-the-temperature-range-of-200%e2%84%83-to-700%e2%84%83-according-to-gb-t-3098-8","status":"publish","type":"post","link":"https:\/\/korea-transmission.com\/fr\/blog\/technical-standards-for-fasteners-in-the-temperature-range-of-200%e2%84%83-to-700%e2%84%83-according-to-gb-t-3098-8\/","title":{"rendered":"Normes techniques relatives aux fixations dans la plage de temp\u00e9ratures de -200\u00a0\u00b0C \u00e0 +700\u00a0\u00b0C selon la norme GB\/T 3098.8"},"content":{"rendered":"
\n

<\/h1>\n
\n

Introduction<\/h2>\n

La norme GB\/T 3098.8 sp\u00e9cifie les propri\u00e9t\u00e9s m\u00e9caniques, les mat\u00e9riaux, les essais, les marques d'identification et le marquage des \u00e9l\u00e9ments de fixation utilis\u00e9s dans les assemblages boulonn\u00e9s fonctionnant dans une plage de temp\u00e9ratures allant de -200 \u00b0C \u00e0 +700 \u00b0C. Cette norme s'applique aux boulons, vis, goujons et \u00e9crous en aciers inoxydables aust\u00e9nitiques, en aciers et en alliages de nickel, garantissant leur fiabilit\u00e9 dans des environnements \u00e0 temp\u00e9ratures extr\u00eames, tels que les applications cryog\u00e9niques et les milieux industriels \u00e0 haute temp\u00e9rature.<\/p>\n

La norme met l'accent sur la conformit\u00e9 aux documents connexes tels que GB\/T 3098.6, GB\/T 3098.15 et DIN EN 10269 concernant les performances des mat\u00e9riaux et les conditions de traitement thermique. Elle fournit des lignes directrices relatives aux classes de performance m\u00e9canique, aux m\u00e9thodes d'inspection et aux associations de mat\u00e9riaux compatibles afin d'atteindre la capacit\u00e9 de charge maximale des assemblages de fixation.<\/p>\n<\/section>\n

\n

Propri\u00e9t\u00e9s m\u00e9caniques<\/h2>\n

Pour les fixations en acier aust\u00e9nitique pouvant fonctionner \u00e0 des temp\u00e9ratures minimales de -200\u00a0\u00b0C, le tableau\u00a01 pr\u00e9sente les groupes d\u2019acier et leurs nuances de performance. Les propri\u00e9t\u00e9s des mat\u00e9riaux doivent \u00eatre conformes aux normes GB\/T\u00a03098.6 et GB\/T\u00a03098.15.<\/p>\n\n\n\n\n\n\n\n\n\n\n
Temp\u00e9rature minimale de fonctionnement continu (approximative)<\/th>\nGroupe Steelun<\/sup><\/th>\nQualit\u00e9 de performance \u2013 Boulons<\/th>\nNote de performance \u2013 Noix<\/th>\n<\/tr>\n<\/thead>\n
-60\u2103b<\/sup><\/td>\nA2L<\/td>\n50<\/td>\n50<\/td>\n<\/tr>\n
A2<\/td>\n<\/tr>\n
A3<\/td>\n70<\/td>\n<\/tr>\n
-200\u2103c<\/sup><\/td>\nA4L<\/td>\n70<\/td>\n<\/tr>\n
A4<\/td>\n80<\/td>\n<\/tr>\n
A5<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Remarque\u00a0: Les temp\u00e9ratures sup\u00e9rieures \u00e0 ces limites n\u2019ont aucune incidence sur l\u2019utilisation. En dessous de ces limites, des tests de performance sont n\u00e9cessaires en fonction des conditions.
\nun<\/sup> Teneur en cuivre \u22641% (selon GB\/T 3098.6 et GB\/T 3098.15).
\nb<\/sup> Pour les boulons \u00e0 t\u00eate.
\nc<\/sup> Pour les goujons.<\/p>\n

Pour les fixations en acier et en alliage de nickel adapt\u00e9es aux hautes temp\u00e9ratures jusqu'\u00e0 +700\u00a0\u00b0C, le tableau\u00a02 d\u00e9taille les temp\u00e9ratures de service applicables selon la norme DIN EN\u00a010269. Les propri\u00e9t\u00e9s des mat\u00e9riaux doivent \u00eatre conformes au tableau\u00a04 de la norme DIN EN\u00a010269 pour les \u00e9tats de traitement thermique. Les donn\u00e9es de r\u00e9f\u00e9rence pour la limite d'\u00e9lasticit\u00e9 0,2% \u00e0 haute temp\u00e9rature, la r\u00e9sistance \u00e0 la rupture par fluage et les propri\u00e9t\u00e9s de relaxation sont fournies dans les tableaux\u00a05, C.1 et D.1 de la norme DIN EN\u00a010269.<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
min<\/th>\n\u00e0 court termeun<\/sup> max<\/th>\n\u00e0 long termeb<\/sup> max<\/th>\nAbr\u00e9viation<\/th>\nNombre<\/th>\nGrade<\/th>\nCondition<\/th>\nDuret\u00e9 HV des boulons et\/ou \u00e9crous<\/th>\n<\/tr>\n
min<\/th>\nmax<\/th>\n<\/tr>\n<\/thead>\n
-120\u2103<\/td>\n\/<\/td>\n\/<\/td>\nKB<\/td>\n1.568<\/td>\nX12Ni5<\/td>\n+NT<\/td>\n157<\/td>\n203<\/td>\n<\/tr>\n
+QT<\/td>\n173<\/td>\n235<\/td>\n<\/tr>\n
\/<\/td>\n400 \u00b0C<\/td>\n500 \u00b0C<\/td>\nYd<\/td>\n1.1181<\/td>\nC35E<\/td>\n+N<\/td>\n150<\/td>\n200<\/td>\n<\/tr>\n
\/<\/td>\n400 \u00b0C<\/td>\n500 \u00b0C<\/td>\nYK<\/td>\n1.1181<\/td>\nC35E<\/td>\n+QT<\/td>\n165<\/td>\n210<\/td>\n<\/tr>\n
\/<\/td>\n400 \u00b0C<\/td>\n\/<\/td>\nYB<\/td>\n1.5511<\/td>\n35B2g<\/sup><\/td>\n+QT<\/td>\n165<\/td>\n210<\/td>\n<\/tr>\n
-60\u2103<\/td>\n500 \u00b0C<\/td>\n550 \u00b0C<\/td>\nKG<\/td>\n1.7218<\/td>\n25CrMo4<\/td>\n+QT<\/td>\n195<\/td>\n240<\/td>\n<\/tr>\n
-100\u2103<\/td>\n500 \u00b0C<\/td>\n\/<\/td>\nGC<\/td>\n1.7225<\/td>\n42CrMo4<\/td>\n+QT<\/td>\n275<\/td>\n337<\/td>\n<\/tr>\n
\/<\/td>\n500 \u00b0C<\/td>\n550 \u00b0C<\/td>\nG\u00e9orgie<\/td>\n1.7709<\/td>\n21CrMoV5-7<\/td>\n+QT<\/td>\n225<\/td>\n272<\/td>\n<\/tr>\n
\/<\/td>\n600 \u00b0C<\/td>\n550 \u00b0C<\/td>\nGB<\/td>\n1.7711<\/td>\n40CrMoV46<\/td>\n+QT<\/td>\n272<\/td>\n320<\/td>\n<\/tr>\n
\/<\/td>\n550 \u00b0C<\/td>\n600 \u00b0C<\/td>\nVe<\/td>\n1.4923<\/td>\nX22CrMoV12-1<\/td>\n+QT1et<\/sup><\/td>\n256<\/td>\n303<\/td>\n<\/tr>\n
\/<\/td>\n550 \u00b0C<\/td>\n600 \u00b0C<\/td>\nVHf<\/sup><\/td>\n1.4923<\/td>\nX22CrMoV12-1<\/td>\n+QT2f<\/sup><\/td>\n287<\/td>\n367<\/td>\n<\/tr>\n
\/<\/td>\n600 \u00b0C<\/td>\n600 \u00b0C<\/td>\nVW<\/td>\n1.4913<\/td>\nX19CrMoNbVN11-1<\/td>\n+QT<\/td>\n287<\/td>\n367<\/td>\n<\/tr>\n
\/<\/td>\n650 \u00b0C<\/td>\n670 \u00b0C<\/td>\nS<\/td>\n1.4986<\/td>\nX7CrNiMoBNb16-16<\/td>\n+WW+P<\/td>\n210<\/td>\n272<\/td>\n<\/tr>\n
-196\u2103<\/td>\n650 \u00b0C<\/td>\n650 \u00b0C<\/td>\nSD<\/td>\n1.498<\/td>\nX6NiCrTiMoVB25-15-2<\/td>\n+AT+P<\/td>\n287<\/td>\n367<\/td>\n<\/tr>\n
-196\u2103<\/td>\n650 \u00b0C<\/td>\n800 \u00b0C<\/td>\nSB<\/td>\n2.4952<\/td>\nNiCr20TiAl<\/td>\n+AT+P<\/td>\n320<\/td>\n417<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Note:
\nun<\/sup> Limite sup\u00e9rieure de temp\u00e9rature pour la limite d'\u00e9lasticit\u00e9 et la r\u00e9sistance \u00e0 la traction.
\nb<\/sup> Limite sup\u00e9rieure de temp\u00e9rature pour la r\u00e9sistance au fluage et \u00e0 la rupture.
\nConditions selon DIN EN 10269 Tableau 4 : +N (normalis\u00e9) ; +NT (normalis\u00e9 et revenu) ; +QT (tremp\u00e9 et revenu) ; +WW (\u00e9croui \u00e0 chaud) ; +AT (recuit de mise en solution) ; +P (durcissement par pr\u00e9cipitation).
\nd<\/sup> R\u00e9serv\u00e9 aux noix.
\net<\/sup> Abr\u00e9viation V selon DIN EN 10269, mat\u00e9riau X22CrMoV12-1, limite d'\u00e9lasticit\u00e9 R de 0,2%p0.2<\/sub> \u2265 600 N\/mm\u00b2 (+QT1).
\nf<\/sup> Abr\u00e9viation VH selon DIN EN 10269, mat\u00e9riau X22CrMoV12-1, limite d'\u00e9lasticit\u00e9 R de 0,2%p0.2<\/sub> \u2265 600 N\/mm\u00b2 (+QT2).
\ng<\/sup> Voir \u00e9galement la fiche technique VdT\u00dcV WB 490.<\/p>\n<\/section>\n

\n

Capacit\u00e9 de charge des assemblages boulonn\u00e9s<\/h2>\n

Exigences g\u00e9n\u00e9rales<\/h3>\n

Un assemblage boulon-\u00e9crou est consid\u00e9r\u00e9 comme ayant une capacit\u00e9 de charge totale s'il r\u00e9pond aux crit\u00e8res suivants\u00a0:
\n\u2013 Le boulon et l\u2019\u00e9crou sont tous deux enti\u00e8rement porteurs, la hauteur de l\u2019\u00e9crou n\u2019\u00e9tant pas inf\u00e9rieure au type 1 pour les filetages grossiers ou au type 2 pour les filetages fins.
\n\u2013 Tol\u00e9rances de filetage appropri\u00e9es, par exemple 6H\/6g.
\n\u2013 R\u00e9sistance \u00e0 la traction du mat\u00e9riau de l\u2019\u00e9crou au moins 70% de r\u00e9sistance \u00e0 la traction du mat\u00e9riau du boulon.
\n\u2013 Correspondance rationnelle des mat\u00e9riaux selon le tableau 3.
\nRemarque : Si des manchons porteurs sont utilis\u00e9s, privil\u00e9giez le m\u00eame mat\u00e9riau que le boulon.<\/p>\n

Choix rationnel des mat\u00e9riaux des boulons et des \u00e9crous<\/h3>\n\n\n\n\n\n<\/p>\n\n\n\n\n\n
<\/th>\nBoulons<\/th>\nNuts Proof Stressun<\/sup> Sp<\/sub> \/ (N\/mm\u00b2)<\/th>\n<\/tr>\n
Aciers inoxydables aust\u00e9nitiques de haute performance<\/th>\nAcier et alliages de nickel<\/th>\nFiletage grossier type 1<\/th>\nFiletage fin type 2<\/th>\n<\/tr>\n
noix<\/th>\nCat\u00e9gorie<\/th>\n50<\/th>\n70<\/th>\nKB<\/th>\nYK<\/th>\nYB<\/th>\nKG<\/th>\nG\u00e9orgie<\/th>\nGB<\/th>\nGC<\/th>\nV<\/th>\nVH<\/th>\nVW<\/th>\nS<\/th>\nSD<\/th>\nSB<\/th>\nGrossier<\/th>\nBien<\/th>\n<\/tr>\n<\/thead>\n
Aciers inoxydables aust\u00e9nitiques de haute performance<\/td>\n50<\/td>\n\u25cb<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n629b<\/sup><\/td>\n725b<\/sup><\/td>\n<\/tr>\n

<\/p>\n

70<\/td>\n\u25cb<\/td>\n\u25cb<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n800b<\/sup><\/td>\n875b<\/sup><\/td>\n<\/tr>\n
80<\/td>\n\u25cf<\/td>\n\u25cf<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n886b<\/sup><\/td>\n950b<\/sup><\/td>\n<\/tr>\n

<\/p>\n

Boulons<\/td>\nR\u00e9sistance \u00e0 la traction Rm<\/sub> \/ (N\/mm\u00b2)<\/td>\nmax<\/td>\n–<\/td>\n–<\/td>\n710<\/td>\n650<\/td>\n650<\/td>\n750<\/td>\n850<\/td>\n1000<\/td>\n1060<\/td>\n950<\/td>\n1050<\/td>\n1050<\/td>\n850<\/td>\n1150<\/td>\n1300<\/td>\n<\/td>\n<\/tr>\n
min<\/td>\n500<\/td>\n700<\/td>\n530<\/td>\n500<\/td>\n500<\/td>\n600<\/td>\n700<\/td>\n850<\/td>\n860<\/td>\n800<\/td>\n900<\/td>\n900<\/td>\n650<\/td>\n900<\/td>\n1000<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

Remarque : \u25cf Correspondance pr\u00e9f\u00e9r\u00e9e ; \u25cb Correspondance autoris\u00e9e ; \u2013 Non recommand\u00e9e.
\nun<\/sup> La contrainte d'\u00e9preuve tient compte d'une duret\u00e9 du mandrin d'essai sup\u00e9rieure \u00e0 celle du boulon correspondant, mais sup\u00e9rieure \u00e0 la r\u00e9sistance \u00e0 la traction minimale du boulon de la plus haute qualit\u00e9.
\nb<\/sup> Contrainte d'\u00e9preuve \u00e9lev\u00e9e pour l'identification des \u00e9crous \u00e0 pleine charge selon GB\/T 3098.15.<\/p>\n

Charges de traction minimales pour les boulons \u00e0 filetage grossier (Tableau 4a)<\/h3>\n\n\n\n\n<\/p>\n\n
Taille du fil d<\/th>\nZone de stress As,nom<\/sub> \/ mm\u00b2<\/th>\nNuances d'acier inoxydable aust\u00e9nitique<\/th>\nAcier et alliages de nickel<\/th>\n<\/tr>\n
50<\/th>\n70<\/th>\nKB<\/th>\nYK\/YB<\/th>\nKG<\/th>\nG\u00e9orgie<\/th>\nGB<\/th>\nGC<\/th>\nV<\/th>\nVH\/VW<\/th>\nS<\/th>\nSD<\/th>\nSB<\/th>\n<\/tr>\n<\/thead>\n
M3<\/td>\n5.03<\/td>\n2.52<\/td>\n3.52<\/td>\n2.67<\/td>\n2.52<\/td>\n3.02<\/td>\n3.52<\/td>\n4.28<\/td>\n4.33<\/td>\n4.02<\/td>\n4.53<\/td>\n3.27<\/td>\n4.53<\/td>\n5.03<\/td>\n<\/tr>\n

<\/tbody>\n<\/table>\n

<\/p>\n

Boulons \u00e0 pleine capacit\u00e9 de charge<\/h3>\n

Les boulons sont enti\u00e8rement porteurs s'ils atteignent les charges de traction minimales selon les tableaux 4a ou 5a, la rupture se produisant dans la longueur filet\u00e9e libre ou la tige non filet\u00e9e selon GB\/T 3098.1 ou GB\/T 3098.6.<\/p>\n<\/section>\n

\n

Foire aux questions (FAQ)<\/h2>\n
\n
Quels mat\u00e9riaux sont recommand\u00e9s pour les fixations \u00e0 -200\u2103 ?<\/dt>\n
Aciers aust\u00e9nitiques tels que A4L, A4 et A5 avec des grades de performance 70 ou 80, conform\u00e9ment au tableau 1, assurant la conformit\u00e9 aux normes GB\/T 3098.6 et GB\/T 3098.15 pour les conditions cryog\u00e9niques.<\/dd>\n
Comment choisir les mat\u00e9riaux des boulons et des \u00e9crous adapt\u00e9s aux applications \u00e0 haute temp\u00e9rature\u00a0?<\/dt>\n
Consultez le tableau 3 pour conna\u00eetre les appariements rationnels. Les appariements recommand\u00e9s (\u25cf) garantissent des performances optimales\u00a0; assurez-vous que la r\u00e9sistance \u00e0 la traction de l\u2019\u00e9crou est au moins \u00e9gale \u00e0 celle du boulon (70%) et que les tol\u00e9rances de filetage sont appropri\u00e9es, par exemple 6H\/6g.<\/dd>\n
Quels tests sont requis pour les fixations en dessous des temp\u00e9ratures minimales sp\u00e9cifi\u00e9es\u00a0?<\/dt>\n
Des tests de performance bas\u00e9s sur des conditions d'utilisation sp\u00e9cifiques, notamment des tests d'impact et de traction, permettent de v\u00e9rifier l'int\u00e9grit\u00e9 au-del\u00e0 des limites de la norme.<\/dd>\n
Existe-t-il des exigences sp\u00e9cifiques en mati\u00e8re de traitement thermique pour les fixations en alliage de nickel\u00a0?<\/dt>\n
Oui, des conditions comme +AT+P pour des nuances telles que SB et SD selon DIN EN 10269 Tableau 4, avec des plages de duret\u00e9 sp\u00e9cifi\u00e9es dans le Tableau 2.<\/dd>\n
Comment v\u00e9rifie-t-on la capacit\u00e9 de charge totale des assemblages\u00a0?<\/dt>\n
Par le biais d'essais de traction permettant d'atteindre les charges minimales des tableaux 4a\/5a pour les boulons et les charges d'\u00e9preuve des tableaux 4b\/5b pour les \u00e9crous, avec des v\u00e9rifications de l'emplacement de la rupture selon les normes GB\/T pertinentes.<\/dd>\n
Quelle est la signification d'une contrainte de preuve \u00e9lev\u00e9e pour les noix aust\u00e9nitiques\u00a0?<\/dt>\n
Il permet d'identifier les \u00e9crous supportant la charge maximale, notamment pour les productions en petites s\u00e9ries, en compensant les inhomog\u00e9n\u00e9it\u00e9s du mat\u00e9riau dues \u00e0 l'\u00e9crouissage.<\/dd>\n<\/dl>\n<\/section>\n<\/div>","protected":false},"excerpt":{"rendered":"

Introduction GB\/T 3098.8 specifies the mechanical properties, materials, testing, identification marks, and markings for fasteners used in bolted connections operating within the temperature range of -200\u2103 to +700\u2103. This standard applies to bolts, screws, studs, and nuts made from austenitic stainless steels, steels, and nickel alloys, ensuring reliability in extreme temperature environments such as cryogenic […]<\/p>","protected":false},"author":2,"featured_media":0,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":{"_et_pb_use_builder":"","_et_pb_old_content":"","_et_gb_content_width":"","footnotes":""},"categories":[220],"tags":[],"class_list":["post-5567","post","type-post","status-publish","format-standard","hentry","category-technical-documentation-and-references"],"_links":{"self":[{"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/posts\/5567","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/comments?post=5567"}],"version-history":[{"count":2,"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/posts\/5567\/revisions"}],"predecessor-version":[{"id":5570,"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/posts\/5567\/revisions\/5570"}],"wp:attachment":[{"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/media?parent=5567"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/categories?post=5567"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/korea-transmission.com\/fr\/wp-json\/wp\/v2\/tags?post=5567"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}