{"id":5561,"date":"2025-12-19T08:38:52","date_gmt":"2025-12-19T08:38:52","guid":{"rendered":"https:\/\/korea-transmission.com\/?p=5561"},"modified":"2025-12-19T08:38:52","modified_gmt":"2025-12-19T08:38:52","slug":"mechanical-performance-standards-for-stainless-steel-fasteners-gb-t-3098-6-2014","status":"publish","type":"post","link":"https:\/\/korea-transmission.com\/es\/blog\/mechanical-performance-standards-for-stainless-steel-fasteners-gb-t-3098-6-2014\/","title":{"rendered":"Normas de rendimiento mec\u00e1nico para elementos de fijaci\u00f3n de acero inoxidable GB\/T 3098.6-2014"},"content":{"rendered":"
\n

La norma GB\/T 3098.6-2014 especifica las propiedades mec\u00e1nicas de pernos, tornillos y esp\u00e1rragos fabricados con aceros inoxidables resistentes a la corrosi\u00f3n, sometidos a ensayos a una temperatura ambiente de entre 10 \u00b0C y 35 \u00b0C. Esta norma se aplica a elementos de fijaci\u00f3n con di\u00e1metros de rosca nominales de entre 5 mm y 100 mm, garantizando un rendimiento fiable en diversas aplicaciones industriales. La norma clasifica los aceros inoxidables en grupos austen\u00edticos, martens\u00edticos y ferr\u00edticos, definiendo clases de propiedades en funci\u00f3n de la resistencia a la tracci\u00f3n, el l\u00edmite el\u00e1stico, la elongaci\u00f3n y la dureza.<\/p>\n

Propiedades mec\u00e1nicas<\/h2>\n

Las propiedades mec\u00e1nicas descritas en la norma GB\/T 3098.6-2014 garantizan que los elementos de fijaci\u00f3n de acero inoxidable cumplan con los requisitos espec\u00edficos de resistencia y ductilidad. Estas propiedades son fundamentales para aplicaciones que requieren resistencia a la corrosi\u00f3n combinada con integridad mec\u00e1nica. La tabla a continuaci\u00f3n detalla los valores m\u00ednimos de resistencia a la tracci\u00f3n (Rm), l\u00edmite el\u00e1stico (Rp0.2), alargamiento tras la fractura (A) y rangos de dureza para diferentes grupos de acero y clases de propiedades.<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Grupo del Acero<\/th>\nGrado de acero<\/th>\nClase de propiedad<\/th>\nResistencia a la tracci\u00f3n Rm (MPa) m\u00edn.<\/th>\nL\u00edmite el\u00e1stico Rp0,2 (MPa) m\u00edn.<\/th>\nAlargamiento A min (en m\u00faltiplos de d)<\/th>\nDureza HB<\/th>\nDureza HRC<\/th>\nDureza HV<\/th>\n<\/tr>\n
m\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\n<\/tr>\n<\/thead>\n
Austen\u00edtico<\/td>\nA1, A2, A3, A4, A5<\/td>\n50<\/td>\n500<\/td>\n210<\/td>\n0,6 d\u00edas<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
70<\/td>\n700<\/td>\n450<\/td>\n0,4 d\u00edas<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
80<\/td>\n800<\/td>\n600<\/td>\n0,3d<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
Martens\u00edtico<\/td>\nC1<\/td>\n50<\/td>\n500<\/td>\n250<\/td>\n0,2d<\/td>\n147<\/td>\n209<\/td>\n–<\/td>\n–<\/td>\n155<\/td>\n220<\/td>\n<\/tr>\n
70<\/td>\n700<\/td>\n410<\/td>\n0,2d<\/td>\n209<\/td>\n314<\/td>\n20<\/td>\n34<\/td>\n220<\/td>\n330<\/td>\n<\/tr>\n
1101<\/sup><\/td>\n1100<\/td>\n820<\/td>\n0,2d<\/td>\n–<\/td>\n–<\/td>\n36<\/td>\n45<\/td>\n350<\/td>\n440<\/td>\n<\/tr>\n
Martens\u00edtico<\/td>\nC3<\/td>\n80<\/td>\n800<\/td>\n640<\/td>\n0,2d<\/td>\n228<\/td>\n323<\/td>\n21<\/td>\n35<\/td>\n240<\/td>\n340<\/td>\n<\/tr>\n
Martens\u00edtico<\/td>\nC4<\/td>\n50<\/td>\n500<\/td>\n250<\/td>\n0,2d<\/td>\n147<\/td>\n209<\/td>\n–<\/td>\n–<\/td>\n155<\/td>\n220<\/td>\n<\/tr>\n
70<\/td>\n700<\/td>\n410<\/td>\n0,2d<\/td>\n209<\/td>\n314<\/td>\n20<\/td>\n34<\/td>\n220<\/td>\n330<\/td>\n<\/tr>\n
Ferr\u00edtico<\/td>\nF12<\/sup><\/td>\n45<\/td>\n450<\/td>\n250<\/td>\n0,2d<\/td>\n128<\/td>\n209<\/td>\n–<\/td>\n–<\/td>\n135<\/td>\n220<\/td>\n<\/tr>\n
60<\/td>\n600<\/td>\n410<\/td>\n0,2d<\/td>\n171<\/td>\n271<\/td>\n–<\/td>\n–<\/td>\n180<\/td>\n285<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

1<\/sup> Templado y revenido a una temperatura m\u00ednima de revenido de 275 \u00b0C.
\n2<\/sup> Para di\u00e1metros de rosca nominales d \u2264 24 mm.<\/p>\n

Composici\u00f3n qu\u00edmica<\/h2>\n

Los requisitos de composici\u00f3n qu\u00edmica de la norma GB\/T 3098.6-2014 definen los l\u00edmites elementales para los grados de acero inoxidable utilizados en elementos de fijaci\u00f3n. Estas composiciones garantizan la resistencia a la corrosi\u00f3n, las propiedades mec\u00e1nicas y la facilidad de fabricaci\u00f3n. La tabla que aparece a continuaci\u00f3n muestra los l\u00edmites porcentuales de los elementos clave en cada grado de acero.<\/p>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
Grado de acero<\/th>\nGrupo del Acero<\/th>\nC (%)<\/th>\nSi (%) m\u00e1x.<\/th>\nMn (%) m\u00e1ximo<\/th>\nP (%) m\u00e1x.<\/th>\nS (%)<\/th>\nN (%) m\u00e1ximo<\/th>\nCr (%)<\/th>\nMo (%)<\/th>\nNi (%)<\/th>\nCu (%)<\/th>\nOtros (%)<\/th>\n<\/tr>\n
m\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\nm\u00edn.<\/th>\nm\u00e1ximo<\/th>\n<\/tr>\n<\/thead>\n
A1<\/td>\nAusten\u00edtico<\/td>\n–<\/td>\n0.12<\/td>\n1<\/td>\n6.5<\/td>\n0.20<\/td>\n0.153<\/sup><\/td>\n0.353<\/sup><\/td>\n–<\/td>\n16<\/td>\n19<\/td>\n–<\/td>\n0.70<\/td>\n5.04<\/sup><\/td>\n10.05<\/sup><\/td>\n1.75<\/td>\n2.25<\/td>\n–<\/td>\n<\/tr>\n
A2<\/td>\n–<\/td>\n0.106<\/sup><\/td>\n1<\/td>\n2.0<\/td>\n0.05<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n157<\/sup><\/td>\n20<\/td>\n–<\/td>\n–8<\/sup><\/td>\n8.0<\/td>\n19.0<\/td>\n–<\/td>\n4.0<\/td>\n–<\/td>\n<\/tr>\n
A39<\/sup><\/td>\n–<\/td>\n0.08<\/td>\n1<\/td>\n2.0<\/td>\n0.05<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n17<\/td>\n19<\/td>\n–<\/td>\n–<\/td>\n9.0<\/td>\n12.0<\/td>\n–<\/td>\n1.0<\/td>\n–<\/td>\n<\/tr>\n
A410<\/sup><\/td>\n–<\/td>\n0.086<\/sup><\/td>\n1<\/td>\n2.0<\/td>\n0.05<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n16<\/td>\n18<\/td>\n2<\/td>\n3<\/td>\n10.0<\/td>\n15.0<\/td>\n–<\/td>\n4.0<\/td>\n–<\/td>\n<\/tr>\n
A59,10<\/sup><\/td>\n–<\/td>\n0.08<\/td>\n1<\/td>\n2.0<\/td>\n0.05<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n16<\/td>\n19<\/td>\n2<\/td>\n3<\/td>\n10.5<\/td>\n14.0<\/td>\n–<\/td>\n1.0<\/td>\n–<\/td>\n<\/tr>\n
C110<\/sup><\/td>\nMartens\u00edtico<\/td>\n0.09<\/td>\n0.15<\/td>\n1<\/td>\n1.0<\/td>\n0.05<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n12<\/td>\n14<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n1.0<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
C3<\/td>\n0.17<\/td>\n0.25<\/td>\n1<\/td>\n1.0<\/td>\n0.04<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n16<\/td>\n18<\/td>\n–<\/td>\n–<\/td>\n1.5<\/td>\n2.5<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
C410<\/sup><\/td>\n0.08<\/td>\n0.15<\/td>\n1<\/td>\n1.5<\/td>\n0.06<\/td>\n0.153<\/sup><\/td>\n0.353<\/sup><\/td>\n–<\/td>\n12<\/td>\n14<\/td>\n–<\/td>\n0.60<\/td>\n–<\/td>\n1.0<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
F111<\/sup><\/td>\nFerr\u00edtico<\/td>\n–<\/td>\n0.12<\/td>\n1<\/td>\n1.0<\/td>\n0.04<\/td>\n–<\/td>\n0.03<\/td>\n–<\/td>\n15<\/td>\n18<\/td>\n–<\/td>\n–12<\/sup><\/td>\n–<\/td>\n1.0<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

3<\/sup> El azufre puede sustituirse por selenio.
\n4<\/sup> Si el contenido de n\u00edquel es inferior a 8%, el contenido m\u00ednimo de manganeso debe ser de 5%.
\n5<\/sup> Si el contenido de n\u00edquel es superior a 8%, no existe l\u00edmite para el contenido m\u00ednimo de cobre.
\n6<\/sup> En aceros austen\u00edticos con un contenido m\u00e1ximo de carbono de 0,03%, puede haber nitr\u00f3geno presente hasta 0,22%.
\n7<\/sup> Si el contenido de cromo es inferior a 17%, el contenido m\u00ednimo de n\u00edquel debe ser de 12%.
\n8<\/sup> El molibdeno puede estar presente a discreci\u00f3n del fabricante. Para algunas aplicaciones, se pueden especificar l\u00edmites en el contenido de molibdeno en el pedido.
\n9<\/sup> Grados estabilizados: contenido de titanio \u2265 5\u00d7C% hasta 0,8%, o niobio y\/o tantalio \u2265 10\u00d7C% hasta 1,0%.
\n10<\/sup> Para productos con di\u00e1metros mayores, con el fin de lograr las propiedades mec\u00e1nicas especificadas, se puede utilizar un mayor contenido de carbono, hasta 0,12% para aceros austen\u00edticos.
\n11<\/sup> Puede contener titanio \u2265 5\u00d7C% hasta 0,8%, o niobio y\/o tantalio \u2265 10\u00d7C% hasta 1,0%.
\n12<\/sup> El molibdeno puede estar presente a discreci\u00f3n del fabricante.<\/p>\n

Preguntas frecuentes (FAQ)<\/h2>\n
\n
1. \u00bfCu\u00e1l es el alcance de GB\/T 3098.6-2014?<\/dt>\n
Esta norma se aplica a pernos, tornillos y esp\u00e1rragos de acero inoxidable con di\u00e1metros de rosca nominales de 5 mm a 100 mm, probados a temperaturas ambiente entre 10 \u00b0C y 35 \u00b0C.<\/dd>\n
2. \u00bfC\u00f3mo se designan las clases de propiedades en esta norma?<\/dt>\n
Las clases de propiedades como 50, 70, 80 y 110 indican la resistencia a la tracci\u00f3n nominal en MPa dividida por 10, adaptada a aceros inoxidables austen\u00edticos, martens\u00edticos o ferr\u00edticos.<\/dd>\n
3. \u00bfQu\u00e9 tratamiento t\u00e9rmico se requiere para el acero martens\u00edtico de grado C1 en la clase de propiedad 110?<\/dt>\n
Para lograr las propiedades mec\u00e1nicas especificadas, debe someterse a un proceso de temple y revenido a una temperatura m\u00ednima de 275 \u00b0C.<\/dd>\n
4. \u00bfExisten restricciones en el di\u00e1metro de la rosca para el acero ferr\u00edtico de grado F1?<\/dt>\n
S\u00ed, las propiedades de F1 se aplican a elementos de fijaci\u00f3n con di\u00e1metros de rosca nominales de hasta 24 mm.<\/dd>\n
5. \u00bfC\u00f3mo aborda la norma la estabilizaci\u00f3n en grados austen\u00edticos como A3 y A5?<\/dt>\n
La estabilizaci\u00f3n se logra mediante la adici\u00f3n de titanio (\u2265 5\u00d7C% hasta 0,8%) o niobio\/tantalio (\u2265 10\u00d7C% hasta 1,0%) para prevenir la precipitaci\u00f3n de carburos y mejorar la resistencia a la corrosi\u00f3n.<\/dd>\n
6. \u00bfSe puede ajustar el contenido de molibdeno en el grado A2?<\/dt>\n
El molibdeno puede a\u00f1adirse a discreci\u00f3n del fabricante, pero deben indicarse l\u00edmites espec\u00edficos en la orden de compra para aplicaciones que requieran un control preciso.<\/dd>\n<\/dl>\n<\/div>","protected":false},"excerpt":{"rendered":"

GB\/T 3098.6-2014 specifies the mechanical properties of bolts, screws, and studs made from corrosion-resistant stainless steels when tested at an ambient temperature range of 10\u00b0C to 35\u00b0C. This standard applies to fasteners with nominal thread diameters from 5 mm to 100 mm, ensuring reliable performance in various industrial applications. It categorizes stainless steels into austenitic, […]<\/p>","protected":false},"author":2,"featured_media":0,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":{"_et_pb_use_builder":"","_et_pb_old_content":"","_et_gb_content_width":"","footnotes":""},"categories":[220],"tags":[],"class_list":["post-5561","post","type-post","status-publish","format-standard","hentry","category-technical-documentation-and-references"],"_links":{"self":[{"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/posts\/5561","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/comments?post=5561"}],"version-history":[{"count":2,"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/posts\/5561\/revisions"}],"predecessor-version":[{"id":5563,"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/posts\/5561\/revisions\/5563"}],"wp:attachment":[{"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/media?parent=5561"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/categories?post=5561"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/korea-transmission.com\/es\/wp-json\/wp\/v2\/tags?post=5561"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}