{"id":5685,"date":"2025-12-24T00:40:41","date_gmt":"2025-12-24T00:40:41","guid":{"rendered":"https:\/\/korea-transmission.com\/?p=5685"},"modified":"2025-12-24T00:40:41","modified_gmt":"2025-12-24T00:40:41","slug":"gb-t-3098-15-2014-stainless-steel-nuts-mechanical-properties","status":"publish","type":"post","link":"https:\/\/korea-transmission.com\/de\/blog\/gb-t-3098-15-2014-stainless-steel-nuts-mechanical-properties\/","title":{"rendered":"GB\/T 3098.15-2014 Mechanische Eigenschaften von Muttern aus Edelstahl"},"content":{"rendered":"

Einf\u00fchrung in den Standard GB\/T 3098.15-2014<\/h2>\n
\n

GB\/T 3098.15-2014 legt die mechanischen Eigenschaften von Edelstahlmuttern f\u00fcr Verbindungselemente fest. Diese Norm gew\u00e4hrleistet Zuverl\u00e4ssigkeit in verschiedenen industriellen Anwendungen durch die Definition von Anforderungen an Kennzeichnung, chemische Zusammensetzung, mechanische Eigenschaften und Pr\u00fcfverfahren. Sie gilt f\u00fcr Muttern aus austenitischem, martensitischem und ferritischem Edelstahl und deckt Leistungsklassen f\u00fcr unterschiedliche Belastbarkeiten und Umgebungsbedingungen ab. Die Einhaltung dieser Norm garantiert, dass die Muttern strenge Kriterien hinsichtlich Festigkeit, Korrosionsbest\u00e4ndigkeit und Dauerhaftigkeit erf\u00fcllen und ist daher f\u00fcr Ingenieure in der Konstruktion und Fertigung unerl\u00e4sslich.<\/p>\n<\/div>\n

\n

Kennzeichnung, Identifizierung und Oberfl\u00e4chenbeschaffenheit<\/h2>\n

Das Kennzeichnungssystem f\u00fcr Edelstahlmuttern besteht aus der Stahlgruppe und der Festigkeitsklasse, getrennt durch einen Bindestrich. Der erste Teil gibt die Stahlgruppe an (A f\u00fcr austenitisch, C f\u00fcr martensitisch, F f\u00fcr ferritisch), gefolgt von einer Zahl, die den Bereich der chemischen Zusammensetzung kennzeichnet. Der zweite Teil repr\u00e4sentiert die Festigkeitsklasse, ausgedr\u00fcckt als 1\/10 der Streckgrenze in MPa f\u00fcr Muttern mit einer H\u00f6he m \u2265 0,8D oder mit einer f\u00fchrenden Null f\u00fcr d\u00fcnnere Muttern (0,5D \u2264 m < 0,8D).<\/p>\n

    \n
  • Beispiel: A2-70 \u2013 Austenitischer Stahl, kaltverformt, Mindeststreckgrenze 700 MPa (f\u00fcr Muttern m \u2265 0,8D).<\/li>\n
  • Beispiel: C4-70 \u2013 Martensitischer Stahl, verg\u00fctet, Mindestdehnspannung 700 MPa.<\/li>\n
  • Beispiel: A2-035 \u2013 Austenitischer Stahl, kaltverformt, Mindeststreckgrenze 350 MPa (f\u00fcr d\u00fcnnere Muttern).<\/li>\n<\/ul>\n

    Austenitische St\u00e4hle mit niedrigem Kohlenstoffgehalt (C \u2264 0,03%) k\u00f6nnen mit einem \u201eL\u201c gekennzeichnet werden (z. B. A4L-80). Passivierte Oberfl\u00e4chen gem\u00e4\u00df GB\/T 5267.4 werden mit einem \u201eP\u201c gekennzeichnet (z. B. A4-80P). Muttern mit einem Nenndurchmesser D \u2265 5 mm m\u00fcssen auf einer Auflagefl\u00e4che oder -seite deutlich gekennzeichnet sein. Die Herstellerkennzeichnung ist, sofern m\u00f6glich, obligatorisch. Die Verpackung muss Herstellerkennzeichnung, Stahlgruppe, Leistungsklasse und Chargennummer gem\u00e4\u00df GB\/T 90.3 enthalten. Sofern nicht anders angegeben, werden die Muttern gereinigt und poliert; eine Passivierung wird zur Verbesserung der Korrosionsbest\u00e4ndigkeit empfohlen.<\/p>\n<\/div>\n

    \n

    Chemische Zusammensetzung<\/h2>\n

    Die chemische Zusammensetzung von Edelst\u00e4hlen f\u00fcr Muttern ist in Tabelle 1 gem\u00e4\u00df GB\/T 3098.6-2014 aufgef\u00fchrt. Hersteller w\u00e4hlen die Zusammensetzungen innerhalb der Gruppen, sofern nichts anderes vereinbart ist. Bei interkristalliner Korrosion ist eine Pr\u00fcfung gem\u00e4\u00df GB\/T 4334 durchzuf\u00fchren; empfohlen werden stabilisierte St\u00e4hle der Typen A3\/A5 oder kohlenstoffarme St\u00e4hle (C \u2264 0,03%) der Typen A2\/A4.<\/p>\n

    \n
    \n
    \n
    <\/div>\n<\/div>\n
    \n
    \n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
    Kategorie<\/th>\nGruppe<\/th>\nChemische Zusammensetzung (Massenanteil)\/%<\/th>\nAnmerkungen<\/th>\n<\/tr>\n
    C<\/th>\nSi<\/th>\nMn<\/th>\nP<\/th>\nS<\/th>\nN<\/th>\nCr<\/th>\nMo<\/th>\nNi<\/th>\nCu<\/th>\nAndere<\/th>\n<\/th>\n<\/tr>\n<\/thead>\n
    Austenitisch<\/td>\nA1<\/td>\n0.12<\/td>\n1<\/td>\n6.5<\/td>\n0.2<\/td>\n0.15~0.35<\/td>\n\u2014<\/td>\n16~19<\/td>\n0.7<\/td>\n5~10<\/td>\n1.75~2.25<\/td>\n\u2014<\/td>\nb,c,d<\/td>\n<\/tr>\n
    A2<\/td>\n0.1<\/td>\n1<\/td>\n2<\/td>\n0.05<\/td>\n0.03<\/td>\n\u2014<\/td>\n15~20<\/td>\n\u2014 e<\/td>\n8~19<\/td>\n4<\/td>\n\u2014<\/td>\nf,g<\/td>\n<\/tr>\n
    A3<\/td>\n0.08<\/td>\n1<\/td>\n2<\/td>\n0.045<\/td>\n0.03<\/td>\n\u2014<\/td>\n17~19<\/td>\n\u2014 e<\/td>\n9~12<\/td>\n1<\/td>\n\u2014<\/td>\nh<\/td>\n<\/tr>\n
    A4<\/td>\n0.08<\/td>\n1<\/td>\n2<\/td>\n0.045<\/td>\n0.03<\/td>\n\u2014<\/td>\n16~18.5<\/td>\n2~3<\/td>\n10~15<\/td>\n4<\/td>\n\u2014<\/td>\ng,i<\/td>\n<\/tr>\n
    A5<\/td>\n0.08<\/td>\n1<\/td>\n2<\/td>\n0.045<\/td>\n0.03<\/td>\n\u2014<\/td>\n16~18.5<\/td>\n2~3<\/td>\n10.5~14<\/td>\n1<\/td>\n\u2014<\/td>\nHi<\/td>\n<\/tr>\n
    Martensitisch<\/td>\nC1<\/td>\n0.09~0.15<\/td>\n1<\/td>\n1<\/td>\n0.05<\/td>\n0.03<\/td>\n\u2014<\/td>\n11.5~14<\/td>\n\u2014<\/td>\n1<\/td>\n\u2014<\/td>\n\u2014<\/td>\nich<\/td>\n<\/tr>\n
    C3<\/td>\n0.17~0.25<\/td>\n1<\/td>\n1<\/td>\n0.04<\/td>\n0.03<\/td>\n\u2014<\/td>\n16~18<\/td>\n\u2014<\/td>\n1.5~2.5<\/td>\n\u2014<\/td>\n\u2014<\/td>\n\u2014<\/td>\n<\/tr>\n
    C4<\/td>\n0.08~0.15<\/td>\n1<\/td>\n1.5<\/td>\n0.06<\/td>\n0.15~0.35<\/td>\n\u2014<\/td>\n12~14<\/td>\n0.6<\/td>\n1<\/td>\n\u2014<\/td>\n\u2014<\/td>\nBi<\/td>\n<\/tr>\n
    Ferritisch<\/td>\nFormel 1<\/td>\n0.12<\/td>\n1<\/td>\n1<\/td>\n0.04<\/td>\n0.03<\/td>\n\u2014<\/td>\n15~18<\/td>\n- J<\/td>\n1<\/td>\n\u2014<\/td>\n\u2014<\/td>\nk,l<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n

    Hinweise: a Maximalwerte, sofern nicht anders angegeben. b Schwefel kann durch Selen ersetzt werden. c Wenn Ni 8%, kein Mindestgehalt an Cu. e Mo optional (Herstellerangabe). f Wenn Cr < 17%, min. Ni = 12%. g F\u00fcr max. C = 0,03%, max. N = 0,22%. h Ti \u2265 5 \u00d7 C% bis 0,8% oder Nb\/Ta \u2265 10 \u00d7 C% bis 1,0%. i Bei gr\u00f6\u00dferen Durchmessern h\u00f6herer C-Gehalt bis zu 0,12% f\u00fcr austenitisches Material. j Mo optional. k Ti \u2265 5 \u00d7 C% bis 0,8%. l Nb\/Ta \u226510\u00d7C% bis 1,0%.<\/p>\n

    Diese Zusammensetzung gew\u00e4hrleistet optimale Korrosionsbest\u00e4ndigkeit und mechanische Festigkeit. In den Anh\u00e4ngen finden sich Beispiele aus ISO-Normen f\u00fcr spezielle Anwendungen.<\/p>\n<\/div>\n

    \n

    Mechanische Eigenschaften<\/h2>\n

    Die mechanischen Eigenschaften m\u00fcssen den Tabellen 2 und 3 entsprechen, um abgenommen zu werden. Dies umfasst die H\u00e4rte (f\u00fcr verg\u00fctete Werkstoffe der Sorten C1, C3 und C4) sowie die Pr\u00fcflastpr\u00fcfung. Nicht alle G\u00fcteklassen sind f\u00fcr alle Muttern geeignet; bitte beachten Sie die Produktnormen.<\/p>\n

    Tabelle 2: Mechanische Eigenschaften \u2013 Austenitische Stahlgruppen<\/h3>\n
    \n
    \n
    \n
    <\/div>\n<\/div>\n
    \n
    \n\n\n\n\n\n\n\n\n\n
    Kategorie<\/th>\nGruppe<\/th>\nLeistungsnote<\/th>\nMindest-Dehngrenze SP\/MPa<\/th>\n<\/tr>\n
    <\/th>\n<\/tr>\n
    N\u00fcsse m\u22650,8D<\/th>\nN\u00fcsse 0,5D\u2264m<0,8D<\/th>\nN\u00fcsse m\u22650,8D<\/th>\nN\u00fcsse 0,5D\u2264m<0,8D<\/th>\n<\/tr>\n<\/thead>\n
    Austenitisch<\/td>\nA1, A2, A3, A4, A5<\/td>\n50<\/td>\n025<\/td>\n500<\/td>\n250<\/td>\n<\/tr>\n
    70<\/td>\n035<\/td>\n700<\/td>\n350<\/td>\n<\/tr>\n
    80<\/td>\n040<\/td>\n800<\/td>\n400<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n
    <\/div>\n<\/div>\n<\/div>\n<\/div>\n

    Tabelle 3: Mechanische Eigenschaften \u2013 Martensitische und Ferritische Stahlgruppen<\/h3>\n
    \n
    \n
    \n
    <\/div>\n<\/div>\n
    \n
    \n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
    Kategorie<\/th>\nGruppe<\/th>\nLeistungsnote<\/th>\nMindest-Dehngrenze SP\/MPa<\/th>\nH\u00e4rte<\/th>\n<\/tr>\n
    <\/th>\n<\/tr>\n
    N\u00fcsse m\u22650,8D<\/th>\nN\u00fcsse 0,5D\u2264m<0,8D<\/th>\nN\u00fcsse m\u22650,8D<\/th>\nN\u00fcsse 0,5D\u2264m<0,8D<\/th>\nHB<\/th>\nHRC<\/th>\nHochspannung<\/th>\n<\/tr>\n<\/thead>\n
    Martensitisch<\/td>\nC1<\/td>\n50<\/td>\n025<\/td>\n500<\/td>\n250<\/td>\n147~209<\/td>\n\u2014<\/td>\n155~220<\/td>\n<\/tr>\n
    70<\/td>\n\u2014<\/td>\n700<\/td>\n\u2014<\/td>\n209~314<\/td>\n20~34<\/td>\n220~330<\/td>\n<\/tr>\n
    110 a<\/td>\n055 a<\/td>\n1100<\/td>\n550<\/td>\n\u2014<\/td>\n36~45<\/td>\n350~440<\/td>\n<\/tr>\n
    C3<\/td>\n80<\/td>\n040<\/td>\n800<\/td>\n400<\/td>\n228~323<\/td>\n21~35<\/td>\n240~340<\/td>\n<\/tr>\n
    C4<\/td>\n50<\/td>\n\u2014<\/td>\n500<\/td>\n\u2014<\/td>\n147~209<\/td>\n\u2014<\/td>\n155~220<\/td>\n<\/tr>\n
    70<\/td>\n035<\/td>\n700<\/td>\n350<\/td>\n209~314<\/td>\n20~34<\/td>\n220~330<\/td>\n<\/tr>\n
    Ferritisch<\/td>\nF1 b<\/td>\n45<\/td>\n020<\/td>\n450<\/td>\n200<\/td>\n128~209<\/td>\n\u2014<\/td>\n135~220<\/td>\n<\/tr>\n
    60<\/td>\n030<\/td>\n600<\/td>\n300<\/td>\n171~271<\/td>\n\u2014<\/td>\n180~285<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n<\/div>\n

    a Abgeschreckt und angelassen, Mindestanlasstemperatur 275 \u00b0C, D\u226424 mm. b Erweicht.<\/p>\n

    Diese Eigenschaften dienen als Grundlage f\u00fcr die Auswahl von Anwendungen, die bestimmte Festigkeitsanforderungen stellen, wobei W\u00e4rmebehandlung und Mutterabmessungen zu ber\u00fccksichtigen sind.<\/p>\n<\/div>\n

    \n

    Testmethoden<\/h2>\n

    H\u00e4rtepr\u00fcfungen f\u00fcr martensitische und ferritische St\u00e4hle erfolgen nach GB\/T 231.1 (HB), GB\/T 230.1 (HRC) oder GB\/T 4340.1 (HV), wobei Vickers als Referenzstandard dient. Die Pr\u00fcfverfahren entsprechen GB\/T 3098.2; die Werte m\u00fcssen innerhalb der in Tabelle 3 angegebenen Bereiche liegen. Belastungsversuche nach GB\/T 3098.2 gew\u00e4hrleisten die Tragf\u00e4higkeit ohne Versagen.<\/p>\n

      \n
    1. H\u00e4rtepr\u00fcfung an vorbereiteten Oberfl\u00e4chen.<\/li>\n
    2. Die Pr\u00fcflast schrittweise anlegen und halten, um die Integrit\u00e4t zu \u00fcberpr\u00fcfen.<\/li>\n
    3. Verwenden Sie kalibrierte Ger\u00e4te, um genaue Ergebnisse zu erzielen.<\/li>\n<\/ol>\n

      Diese Methoden erm\u00f6glichen eine zuverl\u00e4ssige \u00dcberpr\u00fcfung der Mutternleistung in realen Montageumgebungen.<\/p>\n<\/div>\n

      \n

      Anh\u00e4nge: Weitere technische Details<\/h2>\n

      Die Anh\u00e4nge bieten ausf\u00fchrliche Informationen:<\/p>\n

        \n
      • Anhang B: Zusammensetzung von Edelst\u00e4hlen nach ISO 683-13, mit Beispielen f\u00fcr ferritische, martensitische und austenitische Typen.<\/li>\n
      • Anhang D: Werkstoffe zur Reduzierung von durch Chloride verursachter Spannungsrisskorrosion, z. B. X2CrNiMoN17-13-5 mit spezifischen Zusammensetzungen f\u00fcr Hochrisikoumgebungen wie Schwimmb\u00e4der.<\/li>\n
      • Anhang E: Hochtemperatur-Streckgrenzenverh\u00e4ltnisse (z. B. A2\/A4 bei 400 \u00b0C: 70%) und Tieftemperatur-Anwendbarkeit (A2\/A3 bis -200 \u00b0C).<\/li>\n
      • Anhang G: Relative magnetische Permeabilit\u00e4t (z. B. A2 \u2248 1,8, nicht magnetisch im l\u00f6sungsgegl\u00fchten Zustand, kann aber nach Kaltverformung magnetisch werden).<\/li>\n<\/ul>\n

        Konsultieren Sie diese f\u00fcr spezielle Anwendungen, um sicherzustellen, dass die Materialauswahl Risiken wie Korrosion oder magnetische St\u00f6rungen minimiert.<\/p>\n<\/div>\n

        \n

        H\u00e4ufig gestellte Fragen<\/h2>\n
        \n
        Worin besteht der Unterschied zwischen Muttern aus Edelstahl der Klassen A2 und A4?<\/dt>\n
        A2 ist ein austenitischer Allzweckstahl mit guter Korrosionsbest\u00e4ndigkeit, w\u00e4hrend A4 gem\u00e4\u00df den Zusammensetzungen in Tabelle 1 Molybd\u00e4n f\u00fcr eine verbesserte Best\u00e4ndigkeit in chloridhaltigen Umgebungen enth\u00e4lt.<\/dd>\n
        <\/dd>\n
        <\/dd>\n
        Wie w\u00e4hle ich die passende Leistungsklasse f\u00fcr eine Mutter aus?<\/dt>\n
        Die Auswahl erfolgt anhand der Anforderungen an die Streckgrenze und der Mutternh\u00f6he; z. B. G\u00fcteklasse 70 f\u00fcr 700 MPa bei Muttern mit m \u2265 0,8D unter Ber\u00fccksichtigung der Anwendungslasten und der Tabellen 2\/3.<\/dd>\n
        <\/dd>\n
        <\/dd>\n
        Welche Pr\u00fcfungen sind f\u00fcr die Abnahme von Muttern aus Edelstahl erforderlich?<\/dt>\n
        H\u00e4rte f\u00fcr martensitische\/ferritische Gruppen und Pr\u00fcflast f\u00fcr alle, gem\u00e4\u00df Abschnitt 3 Methoden, um die Einhaltung der spezifizierten mechanischen Eigenschaften sicherzustellen.<\/dd>\n
        <\/dd>\n
        <\/dd>\n
        K\u00f6nnen diese Muttern in Hochtemperaturanwendungen eingesetzt werden?<\/dt>\n
        Ja, aber siehe Anhang E bez\u00fcglich der reduzierten Streckgrenze bei erh\u00f6hten Temperaturen; z. B. beh\u00e4lt A2 die Festigkeit 70% bei 400 \u00b0C unter nicht-zyklischer Belastung.<\/dd>\n
        <\/dd>\n
        <\/dd>\n
        Wie l\u00e4sst sich interkristalline Korrosion in austenitischen Muttern verhindern?<\/dt>\n
        Verwenden Sie kohlenstoffarme Varianten (z. B. A4L) oder stabilisiertes A3\/A5, gepr\u00fcft nach GB\/T 4334, wie im Abschnitt \u00fcber die chemische Zusammensetzung empfohlen.<\/dd>\n
        <\/dd>\n
        <\/dd>\n
        Welche Kennzeichnung ist auf der Verpackung erforderlich?<\/dt>\n
        Zur R\u00fcckverfolgbarkeit sind die Herstellerkennung, die Stahlgruppe\/Leistungsklasse gem\u00e4\u00df Abbildung 1 und die Chargennummer gem\u00e4\u00df GB\/T 90.3 anzugeben.<\/dd>\n<\/dl>\n<\/div>","protected":false},"excerpt":{"rendered":"

        Introduction to the GB\/T 3098.15-2014 Standard GB\/T 3098.15-2014 specifies the mechanical properties of stainless steel nuts used in fasteners. This standard ensures reliability in various industrial applications by defining requirements for marking, chemical composition, mechanical performance, and testing. It applies to nuts made from austenitic, martensitic, and ferritic stainless steels, covering performance grades suitable for […]<\/p>","protected":false},"author":2,"featured_media":0,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":{"_et_pb_use_builder":"","_et_pb_old_content":"","_et_gb_content_width":"","footnotes":""},"categories":[220],"tags":[],"class_list":["post-5685","post","type-post","status-publish","format-standard","hentry","category-technical-documentation-and-references"],"_links":{"self":[{"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/posts\/5685","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/comments?post=5685"}],"version-history":[{"count":2,"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/posts\/5685\/revisions"}],"predecessor-version":[{"id":5687,"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/posts\/5685\/revisions\/5687"}],"wp:attachment":[{"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/media?parent=5685"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/categories?post=5685"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/korea-transmission.com\/de\/wp-json\/wp\/v2\/tags?post=5685"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}